Pourable ,Condensation Cure Mold Making RTV2 Silicone Rubber
Condensation tin cure molding silicone rubber, Tin-based silicone, also called condensation-cure silicone, are two-component materials which cure at room temperature (RTV) to flexible, high tear-strength rubbers. Tin cured silicone can be poured onto models or they can be made brush-able by adding a Thixotropic additive. They are ideal for molds where easy release or high temperature resistance is required.
Condensation Cure Mold Making RTV2 Silicone Rubbers can be poured or brush onto products for casting polyurethane,epoxy, polyester resin, gypsum/plaster, cement, waxes, low melt alloys/metals, etc.
• Excellent tear strength
• Very high elongation and flexibility
• Little rate of deformation and shrinkage
• High temperature resist,high tear resist
Physical properties of Condensation Cure Mold Making RTV2 Silicone Rubber
||Mixing Ratio By Weight
||Pot life Time
RTV2 silicone Antioxidant agent,mix ratio with silicone rubber at 0.5%-1%,it can great increase about 30%-100% using times of silicone mold and make the silicone rubber with high heat resistance and solvent resistance.
Thickening agent for silicone rubber for vertical surface application(making brush-on molds)
Preparing the Model
Porous surfaces, such as wood, should be dried and sealed. Also applying a release agent, such as petroleum jelly will aid in easy release of a silicone mold. Because silicone can sometimes bond to surfaces which contain silica, such as glass, cements and natural stone; it is recommended to do a spot test for possible adhesion.
|Elongation at break
|Density at 23℃
|Hardness Shore A
Mixing: Charge 100kg by weight of “Part A” and 3kg by weight of “Part B” into a clean, compatible metal or plastic container. The volume of the container should be 3-4 times the volume of the material to be mixed. This allows for expansion of the siloxane material as it de-gasses. Mix thoroughly by hand or with mixing equipment while minimizing air entrapment until a homogeneous mixture is obtained. This will occur when the material takes on a uniform color with no visible striations. Scrape the sides and bottom of the container thoroughly several times while mixing. Once mixing is complete it is recommended that the material be de-aired 2-3 times by intermittent evacuation for a few minutes to minimize any imperfections due to bubbles in the cured material. Typically after releasing the vacuum 2-3 times the mass will collapse on itself at which time the vacuum should be left on only 2-4 minutes longer.
Dongguan Rongxin Silicone Technology Co., Ltd. was founded in 1999, and is located in Dongguan, Guangdong. We are a professional silicone material manufacturer, integrating the R&D, production and sales. Main products are Condensation molding silion rubber, Addition molding silicone rubber,Addition electronic potting silicone rubber,Condensation electronic potting silicone rubber,leather printing roller silicone rubber,LED strip light silicone rubber,human casting silicone rubber and so on. All of our products are with high quality and have got I S O, RoHS, Reach and SGS certificates. Our customers are from all over the world. If you are interested in our products, please feel free to contact us for further information.
Packing & Delivery
1kg/5kg/20kg/25kg/200kg plastic/iron drum,and please contact your local contact for further information on packaging size and availability. Vacuum bag can take according to users demand.Safety-Avoid contact with mucous membranes and eyes. Best method of cleanup is by wiping with disposable paper towels and washing with waterless hand cleaner, then soap and water. If solvents must be used, denatured ethyl alcohol is best, but should be handled with respect for health and flammability hazards.